I was just saying that the intensive folding process wasn’t nearly as necessary for the euro smiths. Especially, as you said, they had more than enough carbon sources to make up for any deficits in their iron sources.
Once the smith turns the raw material into steel, there was very little difference beyond what the final product needed in hardness/flexibility.
Oh for sure on all points.
I was just saying that the intensive folding process wasn’t nearly as necessary for the euro smiths. Especially, as you said, they had more than enough carbon sources to make up for any deficits in their iron sources.
Once the smith turns the raw material into steel, there was very little difference beyond what the final product needed in hardness/flexibility.